Hot Work Mould Steel AISI H13 / 1.2344 / SKD61 steel
1)Comparable steel: H13(USA, ASTM); DHA1(Datong, Japan); 4Cr5MoSiV1(China); 1.2344(Germany DIN); SKD(Japan, JIS)
2) 1.2344 hot work steel Chemical composition:
3) Delivery condition: EAF or ESR; Hot rolled or forging; Black, machined surface; Anneling, Hardness: HBS≤ 229
4) 1.2344 hot work steel Specification: Round bar: Thickness: 60~350mm, Length: 2500~4000mm.
Flat bar: Thickness: 20~300mm, Width: Under the size of 205~2200mm,
Length: 2500~4000mm.
5) 1.2344 hot work steel Material character: Under upper hot initensity and rigidity; Under middle temperature, have good tenacity, hot tirdness nature and definite wearable; Empty quenching under lower Ao shi ti temperature condition. Small distortion after heat-treatment and so on.
6)Application: Used for making hot squeezing mould, forging mould, embedded lump, like: Alloy, cooper and other alloy and other alloy casting mould
7)Ultrasonic test standards: GB/T6402-1991, CLASS 1
8)Payment terms: Prepay30% deposit, T/T or L/C at sight.
1)Comparable steel: H13(USA, ASTM); DHA1(Datong, Japan); 4Cr5MoSiV1(China); 1.2344(Germany DIN); SKD(Japan, JIS)
2) 1.2344 hot work steel Chemical composition:
3) Delivery condition: EAF or ESR; Hot rolled or forging; Black, machined surface; Anneling, Hardness: HBS≤ 229
4) 1.2344 hot work steel Specification: Round bar: Thickness: 60~350mm, Length: 2500~4000mm.
Flat bar: Thickness: 20~300mm, Width: Under the size of 205~2200mm,
Length: 2500~4000mm.
5) 1.2344 hot work steel Material character: Under upper hot initensity and rigidity; Under middle temperature, have good tenacity, hot tirdness nature and definite wearable; Empty quenching under lower Ao shi ti temperature condition. Small distortion after heat-treatment and so on.
6)Application: Used for making hot squeezing mould, forging mould, embedded lump, like: Alloy, cooper and other alloy and other alloy casting mould
7)Ultrasonic test standards: GB/T6402-1991, CLASS 1
8)Payment terms: Prepay30% deposit, T/T or L/C at sight.
| C | Si | Mn | Cr | Mo | V |
| 0.37-0.42 | 0.90-1.20 | 0.30-0.50 | 4.80-5.50 | 1.20-1.50 | 0.90-1.10 |